Heat Shrink Moulded Shapes

Heat Shrink Moulded Shapes

WRSZT

Heat Shrink Breakout

Manufactured from cross-linked polyolefin. Provide sealing protection and strain relief over multi-core cable crutch, including 2-, 3-, 4-, and 5-core breakout. Coated with adhesive on the body and the fingers to form a watertight seal. Flame-retardant breakouts are available upon customer request. Meeting with varieties of configuration requirements. Shrink temperature: start at 90℃, and fully recovered at 130℃.

Download the manual

Technical Data

Technical Data Specification Table


PropertyTest MethodStandard Value

Insulated 

Breakout

Oil Resistant 

Breakout

Semi-conductive

 Breakou

Tensile StrengthASTM-D-638≥12MPa≥12MPa≥12MPa
Elongation at Break

(120℃,168 hrs

ASTM-D-638≥300%≥300%≥300%

Tensile Strength

after Aging

(120℃,168 hrs)

ASTM-D-638≥10MPa≥10MPa≥10MPa

Elongation at Break

after Aging

ASTM-D-638≥230%≥230%≥230%

Tensile Strength

Variation  

after Dipping

ASTM-D-638-≤20%-

Elongation at Break 

after Dipping

ASTM-D-638-≥230%-
Dielectric StrengthIEC 60243≥15kV/mm​≥15kV/mm
Water AbsorptionISO 62≤0.1%≤0.1%≤0.1%
Volume ResistivityIEC 60093≥1×1013Ω·cm≥1×1013Ω·cm≥1×1013Ω·cm
Brittle TemperatureISO 974-40℃-40℃-40℃
Heat Shock160℃，4hNo CrackNo CrackNo Crack
Hardness(Shore A)ISO 868≥80≥80≥80

​

Cores Spec.As Supplied（mm）After Recovered

Body 

Diameter

(D) Min

Finger

Diameter

(d) Min

Full Length

(L)(±5)

Body

Diameter(D) Ma

Finger

Diameter(d) Max

2-cores 

Breakout

WRSZT2-24/14(0#)

24

12

140

14

5

WRSZT2-38/18(1#)

38

20

145

18

7

WRSZT2-45/22(2#)

45

25

145

22

10

WRSZT2-60/25(3#)

60

35

140

25

11

WRSZT2-70/25(4#)70401402511

Cores 

Spec.

As Supplied（mm）

After Recovered

Body 

Diameter

(D) Min

Finger

Diameter

(d) Min

Full

Length

(L)(±5)

Body

Diameter(D) Ma

Finger

Diameter(d) Max

3-cores 

Breakout

WRSZT3-24/17(-2#)

24

11

140

17

5

WRSZT3-48/22(-1#)

48

18

165

22

7

WRSZT3-58/28(0#)

58

25

180

28

8

WRSZT3-68/37(1#)*☆

68

30


210

37

13

WRSZT3-87/43(2#)*☆

87

39

220

43

16

WRSZT3-106/53(3#)*☆

106

42

2355319

WRSZT3-125/65(4#)*☆

125

58

2456525
WRSZT3-140/65(5#)*☆140652456525

Cores 

Spec.

As Supplied（mm）

After Recovered

Body 

Diameter

(D) Min

Finger

Diameter

(d) Min

Full

Length

(L)(±5)

Body

Diameter(D)

Ma

Finger

Diameter(d)

​Max

4-cores 

Breakout

WRSZT4-38/19(0#)

38

10

125

19

5

WRSZT4-50/25(1#)☆

50

16

135

25

7

WRSZT4-70/32(2#)☆

70

23

185

32

10

WRSZT4-82/46(3#)☆

82

30

210

46

13

WRSZT4-90/46(4#)☆

90

35

210

46

13

WRSZT4-109/54(5#)

109

42

2405418

Cores 

Spec.

As Supplied（mm）

After Recovered

Body 

Diameter

(D) Min

Finger

Diameter

(d) Min

Full

Length

(L)(±5)

Body

Diameter(D)

Ma

Finger

Diameter(d)

Max

5-cores 

Breakout

WRSZT5-42/21(0#)

42

11

130

21

5

WRSZT5-57/30(1#)

57

15

170

30

7

WRSZT5-70/38(2#)

70

23

170

38

9

WRSZT5-90/53(3#)

90

30

180

53

13

WRSZT5-120/48(4#)

120

39

205

48

14

Remark: 1.  * means 3-core semi-conductive breakouts are available upon custom request.

                   2.   ☆ means 3-core or 4-core oil resistant breakouts are available upon custom request.

                   3. The breakout coated with hot-melt adhesive comes in two forms: flat adhesive and  spiral adhesive, which can meet different customer needs. 