Dual Wall Adhesive-Lined Polyolefin Heat Shrink Tubing

Adhesive lined heat shrink tubing with environmental sealing capability for a wide variety of electrical applications, including automotive and marine wire harness, wire splices, breakouts, and connector-to-cable transitions.

Download the manual

​Adhesive lined heat shrink tubing with environmental sealing capability for a wide variety of electrical applications, including automotive and marine wire harness, wire splices, breakouts, and connector-to-cable transitions.

07   SBRS-(4X)G.png

Features

● 4:1 shrink ratio

● Superior sealing against water, moisture or other contaminants

● Ideal for connector sealing covering large diameter differences

● Inner adhesive bonds to plastics, steel and polyethylene

● Continuous operating temperature:-45℃-125℃

● Fully shrink temperature:≥125℃

Technical Data

PropertyTest methodStandard Typical Performance
Tensile strength(MPa)ASTM D2671≥10.412.68
Elongation(%)ASTM D2671≥200448.72
Tensile strength after aging(MPa)UL224 158℃X168hr≥7.311.45
Elongation after aging (%)UL224 158℃X168hr≥100390.41
FlammabilityASTM D2671BPassPass
Dielectric strength(kV/mm)IEC 60243≥1518.25
Volume resistivity(Ω.cm)IEC 60093≥1X10141.86X1014

 

Adhesive

PropertyTest methodStandard Performance
Water AbsorptionASTM D570<0.2%
Softening Point(℃)ASTM E2895±5
Strength of pearing (PE)ASTM D 1000120N/25mm
Strength of pearing (AL)ASTM D 100080N/25mm
SizeExpandedAfter RecoveryStandard Package
InchmmInner   Diameter   Min(mm)Inner   Diameter   Dax(mm)Total Wall Thickness  (mm)Adhesive Thickness  (mm)Spool Length M/spool
5/324.04.01.01.05±0.300.50±0.30200
1/46.06.01.51.15±0.300.50±0.30100
5/168.08.02.01.55±0.300.60±0.3050
1/212.012.03.01.75±0.300.60±0.301.22 OR 25M/Roll
5/816.016.04.02.00±0.300.70±0.301.22 OR 25M/Roll
25/3220.020.05.02.30±0.400.70±0.301.22 OR 25M/Roll
124.024.06.02.60±0.400.75±0.301.22 OR 25M/Roll
1-1/432.032.08.03.00±0.400.90±0.301.22 OR 25M/Roll
252.052.013.03.35±0.500.95±0.301.22 OR 25M/Roll