Description:
RSFR marker sleeve is a flattened, heat-shrinkable tubing intended for wire and cable harness identification. It can also be used for applications where limited fire hazard characteristics are necessary. When RSFR is printed with Woer recommended printers and ink ribbons, the marks remain legible, durable, even when exposed to abrasion, aggressive cleaning solvents, and industrial fluids.
Standard SAE-AS 81531, MIL-STD-202F/Method 215J, UL224，RoHS etc
Features
| Material | The sleeving shall be fabricated from irradiated, thermally stabilized and flame retarded modified polyolefin compound containing no halogens or cadmium in the formulation. |
|---|
| Application range | commercial ， Industrial environment |
|---|
| Operating temperature range | -55---+125 ℃ |
|---|
| Minimum recovery temperature | +125 ℃ |
|---|
| Maximum storage temperature | +50 ℃ |
|---|
| Shrink ratio | 2:1, 3:1 |
| Color | White, Yellow, other color is available if ordered |
|---|
| Printing mode | Single sided printing and Double sided printing formats available |
|---|
| Supplied mode | Either Continuous type or Ladder format type is available |
|---|
| Recommended Printers | Thermal transfer printer |
|---|
| Recommended Ribbons | N85 resin ribbon, Black, 100mm(width)*300m(length) |
|---|
Physic performance
| Property | Unit | Testing Requirement | WOER Results |
|---|
| Tensile strength | MPa | 10.3 | 14.3 |
| Ultimate Elongation | % | 200 | 330 |
| Low temperature flexibility 4 hours at -30±1 ℃ | - | No cracking | Pass(no cracking) |
| Heat shock 4 hours at -250±3 ℃ | - | No cracking, flowing or dripping | Pass(no cracking, flowing or dripping) |
| Dielectric strength | kV/mm | 19.7 | 20 |
| Volume Resistivity | Ω·cm | 1014 | 2.0×1014 |
| Corrosive effect | - | No corrosive | pass |
| Heat aging |
| 168 hours at 158±2 ℃ | Pass(no cracking, print is legible) |
| Print performance | Rubs | SAE-AS 81531 | Pass(legible after 100 rubs) |
| Strokes | MIL-STD-202F | Pass(legible after 100 Strokes) |