SBRS-(2X)G

Dual Wall Adhesive-Lined Heat-Shrink Polyolefin Tubing

Adhesive lined heat shrink tubing with environmental sealing capability

Download the manual

Overview

Overview Dimensions

Features and Application

2:1 shrink ratio
Superior sealing against water, moisture or other contaminants
Inner adhesive bonds to plastics, steel and polyethylene
Out jacket flame retardant
Continuous operating temperature:-45 ℃-125℃
Shrink Temperature:125 ℃

Technical Data

Property	Test method	Standard Performance	Typical Performance
Tensile strength(MPa)	ASTM D 2671	≥ 10.4	11.5
Elongation(%)	ASTM D 2671	≥ 300	450
Tensile strength after aging(MPa)	UL224 158 ℃*168h	≥ 7.3	8.5
Elongation after aging (%)	UL224 158 ℃*168h	≥ 200	350
Dielectric strength(kV/mm)	IEC 60243	≥ 15	17.5
Volume resistivity( Ω.cm)	IEC 60093	≥ 1*1014	2.5* 1014

Adhesive

Property	Test method	Standard Performance
Water Absorption	ASTM D 570	＜ 0.2%
Softening Point( ℃)	ASTM E 28	95
Strength of pearing (PE)	ASTM D 1000	120N/25mm
Strength of pearing (AL)	ASTM D 1000	80N/25mm

Size		AS Supplied	After Recovery			Standard Package
Inch	mm	Internal Diameter (mm)	Internal Diameter (mm)	Total Wall Thickness (mm)	Adhesive Thickness (mm)	Spool Length M/spool
1/16	1.6	1.6	0.8	0.60±0.30	0.30±0.2	200
3/32	2.4	2.4	1.2	0.70±0.30	0.35±0.2	200
1/8	3.2	3.2	1.6	0.70±0.30	0.35±0.2	200
3/16	4.8	4.8	2.4	0.80±0.30	0.40±0.2	100
1/4	6.4	6.4	3.2	0.80±0.30	0.40±0.2	100
5/16	7.9	7.9	3.9	0.90±0.30	0.45±0.2	100
3/8	9.5	9.5	4.8	0.90±0.30	0.45±0.2	50
1/2	12.7	12.7	6.4	0.95±0.40	0.45±0.2	1.22 OR 25M/Roll
5/8	15.9	15.9	7.9	0.95±0.40	0.45±0.2	1.22 OR 25M/Roll
3/4	19.1	19.1	9.5	1.00±0.40	0.45±0.2	1.22 OR 25M/Roll
1	25.4	25.4	12.7	1.10±0.40	0.50±0.2	1.22 OR 25M/Roll
1-1/4	31.8	31.8	15.0	1.15±0.40	0.50±0.2	1.22 OR 25M/Roll
1-1/2	38.1	38.1	19.0	1.25±0.40	0.50±0.2	1.22 OR 25M/Roll
1-3/4	44.5	44.5	22.0	1.35±0.40	0.55±0.2	1.22 OR 25M/Roll
2	50.8	50.8	25.4	1.50±0.40	0.60±0.2	1.22 OR 25M/Roll