AC(Heat Shrink Anode Cap)

AC(Heat Shrink Anode Cap)

Description:                                                                                                                       Detailed Specification Download   

Made of cross linked polyolefin, inner coated with adhesive
Sealing and protecting the critical connection between lead wire and anode
Ideal to avoid premature system failure due to loss of the wire to anode termination
Continuous operation temperature: -45℃ to 105℃

Selection Table
Product
No.
B.D/mm
C.D/mm
B.L(±10%)
/mm
C.L (±10%)
/mm
B.W
(±10%)
/mm
As Supplied (Min)
After Recovered (Max)
As Supplied (Min)
After Recovered
(Max)
AC-2#
65
48
12.5
6.5
76
78
2.4
AC-3B
86
62
12.5
6.5
102
78
2.7
AC-4#
120
100
12.5
6.5
102
78
2.4
AC-4B
112
87
12.5
6.5
102
78
2.4
AC-Φ50
50
30
18.0
6.5
45
100
3.2
AC-Φ86
86
45
18.0
6.5
150
80
3.2
AC-Φ112
112
                 55
18.0
6.5
150
80
3.2
Technical Data
Property
Test Method
Standard Value
Tensile Strength
ASTM-D-2671
≥12MPa
Elongation at Break
ASTM-D-2671
≥300%
Tensile Strength after Aging
ASTM-D-2671
≥10MPa (130℃,168 hrs)
Elongation at Break after Aging
ASTM-D-2671
≥240%(130℃,168 hrs)
Dielectric Strength
IEC 60243
≥20 kV/mm
Volume Resistivity
IEC 60093
≥1014Ω·cm
Longitudinal Shrinkage
ASTM-D-2671
≤10%
Water Absorption
ISO 62
≤0.1%
Eccentricity
≤30%
Stress Cracking Resistance
ASTM-D-1693
No cracking
Fungus and Decay Resistance
ISO 846
Pass

Related Products

ADOBE ACROBAT READER

The Adobe Acrobat PDF reader is required to view and read these documents. To obtain the free reader directly from Adobe, click here and follow the installation instructions.

Woer mansion,North Lanjing Rd,Pingshan,Shenzhen P.R.CHINA
     Email:woer@woer.cn, woer@woer.com      Tel: +86-755-28299123     Fax:+86-755-28299160